Using the fused magnesia and magnesia-calcium sand as the main raw materials of self-flowing gunning mix for large surface, and the composite carbon and ceramic combination method is used for the heat repair of the converter bottom, large and small surface, slag line and other parts.

Send Mail

Hotline:

+86-15838093599

Product Details

Using the fused magnesia and magnesia-calcium sand as the main raw materials of self-flowing gunning mass, and the composite carbon and ceramic combination method is used for the heat repair of the converter bottom, large and small surface, slag line and other parts.

It has the advantages of good fluidity, short sintering time (less than 30 minutes), low smoke pollution and convenient construction.

The hopper is used for feeding and the amount of addition depends on the size of the furnace and the degree of erosion.

Item		JDZLPB-1	JDZLPB-2	JDZLPB-3
Chemical content (%)	MgO ≥	80	75	70
	MgO ≥	80	75	70
	CaO ≥	4	4.5	5
	C ≥	5	5.5	6
	SiO₂ ≤	4	4.5	5
Bulk density (g/cm³) ≥	100℃sintering	2.55	2.3	2.2
Compressive strength (MPa) ≥	100℃sintering	35	30	28
Hardening time	≤ min	20	25	30
Flow value	≥ mm	200	200	200
Remark	The specification is just for reference only. The real products will be tailored to special operation conditions and customer’s special requirements.